明顯產(chǎn)品在生產(chǎn)過(guò)程中難免會(huì)出現(xiàn)一些質(zhì)量問(wèn)題，在鋁板生產(chǎn)過(guò)程中，因?yàn)樵O(shè)備或者人員操作失誤等原因容易出現(xiàn)質(zhì)量問(wèn)題，下面鋁板生產(chǎn)廠(chǎng)家進(jìn)行鋁板使用期間出現(xiàn)三種“傷”原因分析。
Any product will inevitably have some quality problems in the production process. In the aluminum plate production process, quality problems are likely to occur due to equipment or personnel misoperation and other reasons. The aluminum plate manufacturer will analyze the causes of three kinds of "injuries" during the use of aluminum plates.
劃傷：劃傷、擦傷、碰傷是鋁板表面呈現(xiàn)的斷續(xù)或連續(xù)的.單條溝狀傷痕。一般是尖銳物與箔材表面接觸后相對(duì)滑動(dòng)時(shí)產(chǎn)生的。產(chǎn)生的主要原因:軋輥、導(dǎo)輥表面有尖狀缺陷，或粘有硬雜物;剪切、合卷、分切的機(jī)械導(dǎo)輥、導(dǎo)路有尖狀缺陷或枯有雜物。
Scratches: Scratches, scratches and bruises are intermittent or continuous on the aluminum plate surface Single groove scar. It is generally caused by the relative sliding of sharp objects after contacting with the foil surface. The main causes: there are sharp defects on the surface of the roll and guide roll, or there are hard impurities; The mechanical guide roller and guide path for shearing, coiling and slitting have sharp defects or debris.

擦傷:由于物體間棱與面，或面與面接觸后發(fā)生相對(duì)滑動(dòng)或錯(cuò)動(dòng)而在箱材表面造成的成束(或組)分布的傷痕。擦傷產(chǎn)生的主要原因:鋁板在加工生產(chǎn)過(guò)程中，與導(dǎo)路、設(shè)備接觸時(shí)，產(chǎn)生相對(duì)摩擦而造成擦傷;坯料松卷、松層或有燕窩狀端面缺陷;軋制時(shí)張力使用不當(dāng)，開(kāi)卷時(shí)產(chǎn)生層間錯(cuò)動(dòng)而產(chǎn)生擦傷。
Scratch: refers to the bundle (or group) of scars on the surface of box material caused by relative sliding or dislocation between edges and surfaces of objects or after the contact between surfaces. The main causes of scratches are as follows: during the processing and production of aluminum plate, when it contacts with the guide road and equipment, it will produce relative friction and cause scratches; The blank is loose, has loose layers or has bird's nest shaped end defects; Improper use of tension during rolling, interlaminar stagger during uncoiling, resulting in scratches.
碰傷:鋁卷與其他物體相撞后，在箱卷表面或端面產(chǎn)生的傷痕。其表現(xiàn)為表面或端面有部分凹陷。碰傷的主要原因:各生產(chǎn)工序吊運(yùn)或存放不當(dāng);運(yùn)輸及搬運(yùn)過(guò)程中碰傷;鋁箔卷在退火料架或包裝臺(tái)上由其他突出物磕碰而產(chǎn)生傷痕。
Bump: the scar on the surface or end face of the case coil after the aluminum coil collides with other objects. The surface or end face is partially concave. The main causes of bruise: improper hoisting or storage of each production process; Collision during transportation and handling; The aluminum foil roll is bumped by other protrusions on the annealing material rack or packaging table, resulting in scars.
以上就是鋁板生產(chǎn)過(guò)程中常見(jiàn)的問(wèn)題介紹，如果你在采購(gòu)氧化鋁板時(shí)有明顯疑問(wèn)，詳情可咨詢(xún)本公司;本公司擁有多年鋁板定制生產(chǎn)經(jīng)驗(yàn)，擁有集研發(fā)、設(shè)計(jì)、生產(chǎn)經(jīng)驗(yàn)的精英骨干團(tuán)隊(duì)多名，歡迎廣大客商前來(lái)http://www.ganyuedu.com咨詢(xún)洽談業(yè)務(wù)。
The above is the introduction of common problems in the aluminum plate production process. If you have any questions when purchasing aluminum oxide plates, please consult our company for details; The company has many years of experience in aluminum plate customization production, and has more than elite backbone teams with research and development, design, and production experience. We welcome customers to come http://www.ganyuedu.com Consult and negotiate business.